STAINLESS STEEL COIL, FOIL &
STRIP
|
Specialty: Thin and Tempered Coil
|
|
200 * 300 * 400 * PH GRADES <> TEMPERED & ANNEALED <> COIL: .001 to
.250
SLITTING - EDGING - POLISHING - CUT TO
LENGTH |
|
FULL SIZE AND CUT - TO - SIZE SHEET &
PLATE |
|
TEMPERED AND ANNEALED SHEET
----- <> PLATE TO 8"
THICK |
|
*PROCESSED FLAT BAR: .125 x .500 TO 1" x
18" |
|
*Processed Flat Bar is Plate Sheared, Straightened & Edged...
"A significant cost savings vs true flat
bar"
Shearing, Plasma or Water Jet Plate Cutting ...
Machining available on cut-outs.
|
|
SS GRADE |
201 |
202 |
301 |
302 |
304 |
304L |
305 |
316 |
316L |
321 |
347 |
405 |
409 |
430 |
410 6 |
420 6 |
PH17-7 |
|
PHYSICAL
PROPERTIES
|
|
Density(lbs.per cu.in) |
.287 |
.287 |
.290 |
.287 |
.287 |
.287 |
290 |
.286 |
.286 |
.285 |
.290 |
.280 |
.280 |
.278 |
.278 |
.278 |
.282 |
|
Modulus of Elast.
(X10 6 PSI) |
26.6 |
28.6 |
28 |
28 |
28 |
28 |
28 |
28 |
28 |
28 |
28 |
29 |
29 |
29 |
29 |
29 |
29.5 |
|
Electrical
Resistivity 1 |
423 |
427 |
432 |
432 |
432 |
432 |
432 |
444 |
444 |
432 |
438 |
360 |
360 |
360 |
342 |
330 |
480 |
|
Thermal
Conductivity 2 |
9.4 |
9.4 |
9.4 |
9.4 |
9.4 |
9.4 |
9.4 |
9.3 |
9.3 |
9.3 |
9.2 |
- |
- |
13.1 |
14.4 |
14.4 |
9.5 |
|
Coefficient of
Thermal Expansion
3 |
8.9 |
9.7 |
9.4 |
9.6 |
9.6 |
9.6 |
9.6 |
8.9 |
8.9 |
9.3 |
9.3 |
6.0 |
6.0 |
5.8 |
5.5 |
5.7 |
8.5 |
|
Cost Factor 4 |
.87 |
.95 |
.95 |
1.00 |
1.00 |
1.13 |
1.39 |
1.56 |
1.68 |
1.35 |
1.62 |
.88 |
- |
.73 |
.76 |
- |
2.18 |
|
TENSILE STRENGTH (x
1000 PSI) |
|
ANNEALED |
115-135 |
95 Min. |
125-145 |
95-110 |
90-100 |
100 Max. |
85-110 |
90-110 |
65 Nom. |
NA |
70-80 |
80-95 |
95 Nom. |
150 Max. |
|
1/8 HARD |
|
|
|
|
100-120 |
100-120 |
|
|
|
|
95-110 |
|
|
|
|
1/4 HARD |
125-150 |
|
125-150 |
125-150 |
120-135 |
125-150 |
|
|
|
|
125 Min. |
|
|
153
Nom. |
|
1/2 HARD |
150-175 |
|
150-175 |
150-175 |
135-150 |
150-175 |
|
|
|
|
|
|
|
180
Nom. |
|
3/4 HARD |
175-195 |
|
175-200 |
175-195 |
|
|
|
|
|
|
|
|
|
200
Nom. |
|
FULL HARD |
185 Min. |
|
185 Min. |
185-225 |
155-170 |
175-190 |
|
|
|
|
135 Min. |
|
|
220
Nom. |
|
SPRING |
200 Min. |
|
200 Min. |
|
|
|
|
|
|
|
|
|
|
|
|
SPL SPRING 5 |
|
|
280 Min.7 |
|
|
|
|
|
|
|
|
180 Nom. |
230 Nom. |
240
Nom. |
|
YIELD STRENGTH
(x 1000 PSI @0.2%Offset) |
|
ANNEALED |
45-60 |
40 Min. |
40-60 |
38-50 |
35-45 |
40-55 |
30-45 |
40-55 |
40 Nom. |
|
45-60 |
40-60 |
50 Nom. |
65 Max |
|
1/8 HARD |
|
|
|
|
80-100 |
80-100 |
|
|
|
|
90-105 |
|
|
|
|
1/4 HARD |
95-125 |
|
80-100 |
100-130 |
100-120 |
100-130 |
|
|
|
|
120 Nom. |
|
|
94 Nom. |
|
1/2 HARD |
115-150 |
|
100-125 |
130-150 |
115-130 |
140-160 |
|
|
|
|
|
|
|
115
Nom. |
|
3/4 HARD |
140-165 |
|
145-160 |
150-170 |
|
|
|
|
|
|
|
|
|
148
Nom. |
|
FULL HARD |
160-185 |
|
160-200 |
170-210 |
135-160 |
160-180 |
|
|
|
|
130 Nom. |
|
|
190
Nom. |
|
SPRING |
185 Min. |
|
185 Min |
|
|
|
|
|
|
|
|
|
|
|
|
SPL SPRING 5 |
|
|
250 Min 7 |
|
|
|
|
|
|
|
|
140 Nom. |
195 Nom. |
225
Nom. |
|
ELONGATION (% in 2
inches) |
|
ANNEALED |
45 Min. |
40 Min. |
45-75 |
40-65 |
50-66 |
40-65 |
40-71 |
46-58 |
25 Nom. |
|
20-32 |
22-31 |
25 Nom. |
25 Min. |
|
1/8 HARD |
|
|
|
|
20-40 |
30-40 |
|
|
|
|
3-8 |
|
|
|
|
1/4 HARD |
25 Min. |
|
35-60 |
30 Min. |
15-25 |
12-25 |
|
|
|
|
1 Nom. |
|
|
22 Nom. |
|
1/2 HARD |
15 Min. |
|
25-50 |
7-15 |
7-15 |
4-10 |
|
|
|
|
|
|
|
10 Nom. |
|
3/4 HARD |
7 Min. |
|
15-30 |
4-10 |
|
|
|
|
|
|
|
|
|
8 Nom. |
|
FULL HARD |
2 Min. |
|
10-25 |
1-4 |
2-6 |
1-5 |
|
|
|
|
1 Nom. |
|
|
5 Nom. |
|
SPRING |
1 Min. |
|
1 Min. |
|
|
|
|
|
|
|
|
|
|
|
|
SPL SPRING 5 |
|
|
1 Nom.7 |
|
|
|
|
|
|
|
|
15 Nom. |
8 Nom. |
6
Nom. |
|
1. OHMS/CIR. MIL FT 2.BTU PER SQ. FT. PER HR. PER F @68F 3.
INCHES PER INCH x 10 to the -6 FROM 32F- 212F 4. DISREGARD 5. TYPICAL HEAT
TREATED PROPERTIES OF MARTENSITIC & PH STAINLESS STEELS 6. GENERALLY SOLD IN
ANNEALED COND. 7. SPECIAL ROLLED SPRING TEMPER
Above figures are theoretical
|
|